Preparation of copper nanoparticles by radiation

Preparation of copper nanoparticles by radiation 1 first-author 1 2 corresp Corresponding author. E-mail address: fujj@zju.edu.cn Corresponding author. E-mail address: fujj@zju.edu.cn fujj@zju.edu.cn 2 1 2 2 Zhejiang Insitute of Application Energy and Nuclear Technology, Hangzhou 310012, China Zhejiang Insitute of Application Energy and Nuclear Technology, Hangzhou 310012, China The Institute of Nuclear Agriculture Science, Zhejiang University, Hangzhou 310021, China The Institute of Nuclear Agriculture Science, Zhejiang University, Hangzhou 310021, China Copper nanoparticles were successfully synthesized by 60 Co-γ radiation with aqueous solution of cupric sulfate under inert nitrogen-purged conditions. Cu nanoparticles were characterized by using X-ray diffraction (XRD), transmission electron microscopy (TEM), laser particle size distribution analyzer (LSPSDA) and differential scanning calorimeter (DSC) techniques, respectively. The effects of solution system, pH, additive of surfactant and absorbed doses on the particle size and its distribution as well as stored stability of Cu naoparticles were investigated. High resolution TEM pictures showed the formation of homogeneous cubic-structured copper nanoparticles with different sizes depends on the synthetic conditions. This new kind of synthesis method shows the excellent stability, which may provide an efficient way to improve the fine tuning of the structure and size of copper nanoparticles. 60 Co-γ radiation Copper nanoparticle Characterization 1 Introduction 1 Due to the unique properties of Metallic Cu, such as interesting optical, electronic, magnetic and chemical properties, Cu nanoparticles are widely used in the fields of lubrication additives, conductive paste, antibacterial agent, information storage, effective catalyst, photoelectricity, etc. The synthesis of copper nanoparticles can be performed by physical gas deposition, electrochemical deposition, decomposition of organic metal compounds, liquid phase reduction, hydrothermal and microemulsion methods and so on. A burst of research activities is reported in the area of synthesis and fabrication of different sizes and shapes of Cu nanoparticles. However, the reproductive method for synthesis of copper nanoparticles with a specific size and well defined surface composition with long storage time remain a challenging task. Very little work has been carried out on the cold synthesis of copper nanoparticles. We have attempted the synthesis of size-controlled copper nanoparticles through a simple aqueous system using 60 Co-γ radiation. 2 Experimental 1 2.1 Materials 2 CuSO 4 , AR, is from Chemical Co. Ltd. of Wenzhou. Isopropyl alcohol (IPA), AR, is from Shuanglin Chemical Co. Ltd. of Hangzhou. Absolute ethyl alcohol, AR, is from Damao Chemical Co. Ltd. of Tianjin. Polyving akohol (dynamic viscosity 54.0-66.0 mPa·s -1 ), AR, is from National Chemical Co. Ltd. 25% aqueous ammonia, CP, is from Dafang Chemical Co. Ltd. of Hangzhou. Acetic amine, AR, is from Hewei Chemical Co. Ltd. of Shanghai. Dodecyl mercaptan, CP, is from Shanghai Chemical Co. Ltd. of National Medicine Company. Sodium dodecyl benzensulfate (SDBS), CP, is from Guanghua Chemical Co. Ltd. of Shantou. NNHDA, dodecyl alcohol amine, CP, is from Yinghu Chemical Co. Ltd. of Hangzhou. Sodium carboxyl methyl cellulose, CP, is from Chemical Co. Ltd. of National Medicine Company. Oleamide, CP, is from Shentong Chemical Co. Ltd. of Zhibo. Oleic acid, CP, is from Shuanglin Chemical Co.Ltd. of Hangzhou. 2.2 Facility and instruments 2 Irradiation was performed by 10 5 Curie 60 Co-γ source at Irradiation Center Facility of Zhejiang University. The crystal phase was determined by use of X Pertpro (XRD, Cu K a λ =1.541 Å). Morphology and particle size were measured by use of JEM-1230 transmission electron microscope (TEM). Particle size and its distribution were measured by use of NaNo ZS-90 (LSPSDA) and the melting point of Cu particles with different sizes was used SDT Q600 (DSC). And KQ-50DA ultrasonic disperse instrument, TG20M centrifuge; DZF-6050 vacuum oven and 85-2 magnetic whisk were used for treatment of samples. 2.3 Preparing process of samples 2 Amount of aqueous solution of surfactant (PCM) was added in aqueous solution of CuSO 4 , prepared by use of CuSO 4 . 5H 2 O, under churn up condition and then amount of isopropyl alcohol was added as scavenger of OH· radical produced from radiolysis of water. The pH of the solution for irradiation was adjusted to be 6.5 by use of NH 4 OH-NH 4 AC and deoxygenated by bubbling with N 2 for 30 minutes. The irradiation for preparing Cu nanoparticles was performed by use of 10 5 Curie of 60 Co-γ with different absorbed doses. The colour of solution was changed from blue into purplish red after irradiation. The upper solution of irradiated sample was toppled out after centrifugal separation and then deactivation agent was added into remained solution to prevent the Cu nanoparticles from oxidation. After alternately several washes by use of deionized water and absolute ethyl alcohol free from O 2 the sample was dried at 60ºC and −0.01 Pa and stored in a small reagent bottle filled with high pure N 2 for further characterization. The reduction of copper cations can be described as follow: <math display="block" id="M1"><mrow><msub><mtext>H</mtext><mn>2</mn></msub><mtext>O</mtext><mo>~</mo><mtext>γ</mtext><mo>−</mo><mtext>rays</mtext><mo>→</mo><msub><mtext>e</mtext><mrow><mtext>aq</mtext></mrow></msub><msup><mrow/><mo>−</mo></msup><mo>,</mo><mtext> H</mtext><mo>⋅</mo><mo>,</mo><mtext>OH</mtext><mo>⋅</mo><mo>,</mo><msub><mrow><mtext> H</mtext></mrow><mn>3</mn></msub><msup><mtext>O</mtext><mo>+</mo></msup><mo>,</mo><msub><mrow><mtext> H</mtext></mrow><mn>2</mn></msub><mo>,</mo><msub><mrow><mtext> H</mtext></mrow><mn>2</mn></msub><msub><mtext>O</mtext><mn>2</mn></msub></mrow></math> <math display="block" id="M2"><mrow><mtext>OH</mtext><mo>⋅</mo><mo>+</mo><mtext>iso</mtext><mo>−</mo><mtext>PrOH</mtext><mo>→</mo><mtext>iso</mtext><mo>−</mo><mtext>PrO</mtext><mo>⋅</mo><mo>+</mo><msub><mtext>H</mtext><mn>2</mn></msub><mtext>O</mtext></mrow></math> <math display="block" id="M3"><mrow><msup><mrow><mtext>Cu</mtext></mrow><mrow><mn>2</mn><mo>+</mo></mrow></msup><mo>+</mo><msub><mtext>e</mtext><mrow><mtext>aq</mtext></mrow></msub><msup><mrow/><mo>−</mo></msup><mo stretchy="false">(</mo><mtext>H</mtext><mo>⋅</mo><mo>,</mo><mtext> iso</mtext><mo>−</mo><mtext>PrO</mtext><mo>⋅</mo><mo stretchy="false">)</mo><mo>→</mo><msup><mrow><mtext>Cu</mtext></mrow><mo>+</mo></msup><mo>+</mo><msub><mtext>e</mtext><mrow><mtext>aq</mtext></mrow></msub><msup><mrow/><mo>−</mo></msup><mo>→</mo><mtext>Cu</mtext><mo>+</mo><mi>n</mi><mtext>Cu</mtext><mo>→</mo><mtext>Cu nanoparticles</mtext></mrow></math> The radiolytical products of water, such as e aq - , H· [ 1 1 ] can effectively reduce the cation of copper meanwhile the iso-PrO· formed from scavenging of OH· by isopropyl alcohol as shown in reaction (2) can also reduce it. Some Cu atoms accumulated to form a crystal and grew to form a nanoparticle [ 2 2 , 3 3 ] . 3 Results and discussion 1 3.1 Effect of surfactants on the properties and size of Cu nanoparticles 2 In order to make the decentrality and stability of Cu atoms formed in irradiated solution, different kinds of surfactants, such as polyving akohol, sodium dodecyl benzensulfate, polypropylene pyrrolidone, polyacryl- amide, Tween 80, sodium alginate and PCM, were used in the preparing solution with 1.0 g/100 mL surfactant, 0.05 mmol·L ‒1 CuSO 4 , 2 mol·L ‒1 IPA, at pH adjusted by NH 4 OH/NH 4 AC for irradiation and the results were listed in Table 1 Table 1 . 1 1 Samples 1 1 Surfactant 1 1 Absorbed doses / kGy 1 1 Aspect of solution 1 1 1 1 1 Polyving akohol 1 1 100 1 1  Purplish red  1 1 2 1 1 sodium dodecyl benzensulfate 1 1 100 1 1 Purplish red 1 1 3 1 1 polypropylene pyrrolidone 1 1 100 1 1 Purplish red 1 1 4 1 1 polyacrylamide 1 1 100 1 1 Black bulk sediment 1 1 5 1 1 Tween 80 1 1 100 1 1 Black sediment 1 1 6 1 1 sodium alginate 1 1 100 1 1 Black sediment 1 1 7 1 1 PCM 1 1 100 1 1 Purplish red, stable The colour of solution was all blue with additive of different surfactants before irradiation. In the sample 1, 2 and 3, Cu 2+ could be reduced to form purplish red Cu nanoparticles [ 4 4 ] under radiation. However, the solution got to become black within 20 minutes after irradiation, which meant that reduced Cu was transferred into Cu 2 O via oxidation in air condition. In sample 4, 5 and 6, the solution presented black and some black sediment were observed just after irradiation, which meant that the 3 kinds of surfactants could not protect reduced Cu from oxidation in radiation process and the particle might be composition of Cu 2 O or Cu 2 O+Cu [ 5 5 ] . In contrast, with the solution system by use of PCM prepared by our group the purplish red Cu nanoparticles with very excellent stability were obtained as the residues of the surfactant PCM had both carboxyl and amide groups, which made the Cu nanoparticles with good distribution and protection from oxidation. Thus the surfactant PCM was always used for preparation of Cu nanoparticles in this study. The effect of different concentrations of surfactants on the Cu nanoparticle size was also investigated by characterization with LSPSDA and TEM. As shown in Figs.1 and 2, the particle sizes and distributions decreased with the increment of concentration of PCM and the sample presented circular and with good distribution. The average particle size was 122.4 nm when the concentration of PCM was 0.6 g/100 mL, and it was 21.3 nm when the concentration of PCM was 2.2 g/100 mL. It can be supposed that the PCM absorbed on the surface of Cu nanoparticle might form electric double layer, which makes the particle very stable in the solution or air and protects it from oxidation [ 6 6 ] . 3.2 Relationship between the size and melting point of Cu nanoparticles 2 Generally, the melting point of material is defined as the temperature at that the equilibrium between solid and liquid of pure material will occur at fixed pressure. And the change of free energy for transfer process of phase is suitable for the equation Δ G =0. To the solid of pure material with highest degree of dispersion, such as nanoparticle, its chemical potential must be related with its particle size [ 7 7 ] though the potential is a function both of pressure and temperature. So the melting point of Cu nanoparticle with different particle sizes can be used to describe its properties. Here, the DSC was used to determine the melting point of Cu nanoparticle with particle size of 122.4 nm, 91.2 nm, 58.9 nm, 28.0 nm and 21.3 nm, respectively. The results were shown in Fig.3 Fig.3 . As shown in Fig.3 Fig.3 , along with the decrement of the particle size the melting point of Cu nanoparticles decreases. When its particle size is 122.4 nm its melting point is 439.71ºC, and when the particle size is 21.3 nm and its melting point is 139.9ºC, which is deeply lower than 1083.4℃ of general Cu. 3.3 Effect of pH on the phase of Cu nanoparticles 2 The chemical property of Cu nanoparticles is very active as E 0 Cu 2+ /Cu=0.337 V. It means that there may be some Cu 2 O exists in the Cu nanoparticle formed from reduction of Cu 2+ in solution induced by γ-rays. Of course, the pH of the solution may play important role in the reductive process. XRD was used to determine the phase of Cu nanoparticles obtained at pH of 3.6, 5.1, 6.0, 7.2 and 9.5, respectively. As shown in Fig.4 Fig.4 , the X-diffraction angles, 2 θ , with samples of a, b, c and d are 43.53º, 50.24º, 74.91º and 89.88º, which are well according with standard X-diffraction angles of Cu listed in the card of 01-085-1326 as characteristic parameter. It can be indicated that the Cu nanoparticles formed with these pH are all composition of pure Cu. When the solution at pH of 7.2 and 9.5 was engaged, besides the X-diffraction angles of pure Cu, 2θ of 36.35º and 61.36º, according to the characteristic X-diffraction angles of Cu 2 O listed in card of 00-005-0667, X-diffraction peak was also observed, which meant that Cu 2 O exactly formed. And the amount of Cu 2 O would increase with the increment of pH value. Anyway, there was no characteristic X-diffraction peaks of CuO in our study. 3.4 Effect of absorbed doses on the formation of Cu nanoparticles 2 As shown in Fig.5 Fig.5 (a), the upper solution of irradiated sample with absorbed doses of 50 kGy remained blue after centrifugal separation, which meant that a part of Cu 2+ had not been reduced completely. But the Cu nanoparticles with good distribution and small particle size formed besides a little of them with non-complete particles could be observed. When the absorbed dose was 150 kGy, the colour of upper solution became transparent from amaranth of irradiated sample after centrifuging meanwhile the obtained Cu nanoparticles revealed good distribution with small size as shown in Fig.5 Fig.5 (b). However, as shown in Fig.5 Fig.5 (c), some accumulation could be observed in obtained Cu nanoparticles from the sample irradiated with absorbed doses of 300 kGy, and the particle size became larger though the Cu 2+ was completely reduced. When the absorbed dose was 500 kGy shown in Fig.5 Fig.5 (d), there was serious accumulation in Cu nanoparticles. It can be deduced that surface electric charge of Cu nanoparticles modified by surfactant may lose because of radiolytical decomposition of surfactants at higher absorbed doses. 3.5 Effect of deactivation on the storage performance of Cu nanoparticles 2 The metallic nanoparticles can be easily oxidized in air, so the deactivation of Cu nanoparticles was made by use of six kinds of compounds, such as NNHDA {C 11 H 23 CON(CH 2 CH 2 OH) 2 }, dodecyl mercaptan, stearic acid, oleic acid, oleamide and castor oil. The deactivated sample was then put in air or alcohol for storage and the diffraction peak of Cu 2 O was detected by XRD to identify if the Cu nanoparticle was oxidized at different storage time. In Fig.6 Fig.6 , with the samples being free from any deactivation stored in air (a) or alcohol (b) for 5 days, the characteristic diffraction peaks at 2 θ of 36.40 and 61.3 were observed and the peaks in air were higher than that in alcohol, which meant that a part of Cu nanoparticles were oxidized to Cu 2 O, especially in the air. Accordingly, the samples deactivated by stearic acid (c), oleic acid (d), oleamide (e), castor oil (f) and NNHDA (g) were also found to be oxidized but that of NNHDA was weaker compared with others. Only the sample deactivated by dodecyl mercaptan (h) was without any characteristic diffraction peaks of Cu 2 O as there were characteristic diffraction peaks of pure Cu (2 θ =43.35, 50.49, 74.11 and 89.88). When the storage time was set up 42 days in alcohol, the characteristic diffraction peaks of Cu 2 O in the sample deactivated by NNHDA disappeared, which may be due to the reduction of Cu 2 O by the active H· in molecule of NNHDA. However, the sample deactivated by stearic acid, oleic acid, oleamide and castor oil remained oxidized state except the sample deactivated by dodecyl mercaptan. Considering that both of NNHDA and dodecyl mercaptan could effectively protect Cu nanoparticles from oxidation, prepared Cu nanoparticles were put into NNHDA and dodecyl mercaptant for storage test with 140 days and it was found that there was no characteristic diffraction peaks of Cu 2 O with only that of pure Cu in the determination using XRD as shown in Fig.7 Fig.7 . It means the two compounds can be used to protect Cu nanoparticles effectively. Compared with dodecyl mercaptant, NNHDA is soluable in water, free of poison and cheaper so it has been selected to protect Cu nanoparticles from oxidation and keep them for further study and application. 4 Conclusion 1 The Cu nanoparticles can be prepared by irradiation of CuSO 4 aqueous solution at room temperature without any additive. The determination using XRD, TEM and DSC has been revealed that samples of Cu nanoparticles with colour amaranth, particle size less than 100 nm and melting point of 139.90ºC are globe powder of pure copper. The surfactants of PCM added in reaction system can make the Cu nanoparticles with good dispersal and the particle size decreases with the increment of concentration of PCM, which can be used to control the particle size and its distribution. The effect of pH of reaction system on the formation of Cu nanoparticles has been investigated. It is better that preparing Cu nanoparticles should be performed in the pH range of 4.0–6.5 since Cu 2 O will form if pH > 7.2 and the reduction of Cu 2+ canot be completed if pH < 4. The absorbed doses for preparing Cu nanoparticle are in the range of 150 kGy–250 kGy. NNHDA, as deactivation agent, can protect Cu nanoprticles from oxidation even when the storage time was more than 140 days. And the productivity of Cu nanoparticles is 89%. Reference Chen Y K , Rao W H , Zhou R M . Chem Eng , 2007 , 12 : 4 - 6 . Chem Eng Huang J S , Ren S , Cai J W . J Guangdong Univ Tech , 2005 , 22 : 16 - 20 . J Guangdong Univ Tech Liu Y P , Zhang M W , Qian Y T , et al . J Radiat Res Radiat Proces , 1997 , 15 : 193 - 200 . J Radiat Res Radiat Proces Qu J R , Hu M A , Chen J Z , et al . Earth Sci - J China Univ Geosci , 2005 , 30 : 195 - 198 . Earth Sci - J China Univ Geosci Robert J W , Alexei K P . Applied Radiation Chemistry: Radiation Processing , New York (USA) : Wiley , 1993 : 165 - 171 . Applied Radiation Chemistry: Radiation Processing Stribeck N . Colloid Polym Sci , 2002 , 280 : 254 - 259 . Colloid Polym Sci Zhang X F , Yin H B , Cheng X N , et al . Chin J Nonfer Metal , 2006 , 16 : 327 - 332 . Chin J Nonfer Metal 10.13538/j.1001-8042/nst.2013.06.004 2012-12-12 2013-12-01 2021-04-11 2013 Nuclear Science and Techniques 6 24