In-situ high energy resolution X-ray absorption spectroscopy for UO₂ oxidation at SSRF

In - situ high energy resolution X-ray absorption spectroscopy for UO 2 oxidation at SSRF 1 first-author 1 1 1 1 corresp Corresponding author, huangyuying@sinap.ac.cn Corresponding author, huangyuying@sinap.ac.cn huangyuying@sinap.ac.cn Shanghai Synchrotron Radiation Facility, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201204, China Shanghai Synchrotron Radiation Facility, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201204, China Based on the high energy resolution fluorescence spectrometer on the BL14W1 beamline at Shanghai Synchrotron Radiation Facility (SSRF), an in - situ high energy resolution X-ray absorption spectroscopy technique, with an in - situ heating cell, was developed. The high energy resolution fluorescence detection for X-ray absorption near-edge spectroscopy (HERFD-XANES) was tested in a UO 2 oxidation experiment to measure the U L 3 -edge, with higher signal-to-noise ratio and higher energy resolution than conventional XANES. The technique has potential application for in - situ study of uranium-based materials. X-ray absorption spectroscopy (XAS) in - situ cell UO 2 oxidation. 1 Introduction 1 As a general nuclear fuel, uranium dioxide has been studied for 50 years, being concentrated on oxidation under different temperatures, oxygen pressure and so on [ 1 1 ] . Temperature is the main condition of oxidation process. Properties of the oxidation products change distinctively with temperature, such as the chemical valence, electronic structure and crystal structure. As temperature increases, UO 2 with a florite crystal type forms a series of valence mixed oxidation products: U 3 O 7 /U 4 O 9 ,U 3 O 8 [ 2 2 ] . This process occurs in the nuclear fuel cycle, transport and waste disposal, with a risk of the volume increase. For example, The final oxidation product U 3 O 8 has a 36% net volume increase over UO 2 due to remarkable difference of crystalline structure and the decreased U/O ratio. To avoid this risk, the uranium dioxidation processes under different tempertures should be studied in advance. X-ray absorption near-edge spectroscopy (XANES) in fluorscence mode is an advanced technique for acquiring information about the chemical valence state and electronic structure of actinide elements. XANES require not much on the probed samples, and its high penetrating power allows bulk detection and in - situ measurement [ 3 3 ] . For detecting valence state of L edge of actinide elements, however, conventianl XANES is limited by the excessively broad spectra width originating from the shorte 2p core hole lifetime. By collecting the Lα emission line, hhigh energy resolution fluorescence detection for X-ray near-edge absorption spectroscopy (HERFD-XAS) performs much better in energy resolution than conventional XAS. HERFD-XAS stations have been established worldwide in increasing numbers [ 4 4 ] during the past two decades, and in the recent years, several groups began their efforts of using this method to study chemical states and electronic structure of actinide elements [ 5 5 , 6 6 ] . The broad width of L 3 edge HERFD-XAS at Lα line originating from the core hole lifetime of 3d is longer than 2p, so some details of the spectra could be extracted [ 7 7 ] . The white line of XAS could provide the information of unoccupied 6d states. The shift of white line is limited to the spectrum width, and narrow white line of HERFD-XAS could obtain more precise structure or the small variation of 6d states [ 8 8 , 9 9 ] . Furthermore, most of the chemical properties of actinide is related to the 5f states [ 10 10 ] . The pre-edge peaks of actinide elements HERFD-XAS originating from transition from 2p to 5f could provide the information of valence state of 5f [ 11 11 ] . T.Vitova and co-workers studied different valence of urinium oxides [ 12 12 ] . The HERFD-XAS of three standard samples illustrated the differerce among U 4+ , U 5+ andU 6+ . The energy resolution at U L 3 of conventional XAS is about 14 eV, while it was 9 eV for HERFD-XAS. This improved energy resolution provided precise analysis about valence changes. The energy resolution power of U L 3 HERFD-XAS is limited by energy resoluton of the incident beam, the spectrometer and the nature broadening related to the lifetime of 3d corehole. The nature broadening of uranium M 4,5 edge is about 3 eV, so the energy resolution of U L 3 HERFD-XAS must be better than 3 eV. Under these conditions, the chemical shift ( < 3 eV) cannot be detected by L 3 edge HERFD-XAS. Therefore, the HERFD-XAS of U M 4 -edge with high energy resolution [ 13 13 ] was developed. The X-ray of U M 4 -edge is too soft to penetrate the gas atmosphere in in - situ study [ 14 14 ] , so the hard X-ray of U L 3 -edge, of good penetrability, is suitable for the HERFD-XAS technique in in - situ environment. A high resolution X-ray fluorescence spectrometer based on Rowland circle geometry on BL14W1 at SSRF has been established [ 15 15 ] for X-ray emission spectroscopy and HERFD-XANES. In this paper, HERFD-XANES data of U L 3 -edge with high signal-to-noise for UO 2 oxidation are obtained, by using the in - situ high-energy resolution X-ray absorption spectroscopy with an in - situ heating cell. 2 Experiments 1 The crystal structures of the UO 2 sample before and after in - situ oxidation were characterized with powder X-ray diffraction (XRD) on a Bruker D8 Advance X-ray diffractometer using the Ni-filtered Cu Kα radiation source at 40 kV and 40 mA, performed on the BL14W1 beamline at SSRF [ 16 16 ] {Yu, 2015 #4}. The incident beams were from a pair of Si(311) reflection crystal monochromator. Little mismatch of the monochromator was performed for the rejection of higher harmonics. The flux at the sample position could reach to 3×10 12 photos/s. The energy calibration was achieved at Zr-L3 absorption edge (17998 eV). As shown in Fig 1(a) Fig 1(a) , the sample was placed in the in - situ heating cell, and the centers of the cell, crystal and detector were on the Rowlan circle. The X-ray beams were from a bending crystal Ge (777) (1 m in curvature radius) and the energy resolution could be down to 2.4 eV with the convolution of incident energy. The XANES spectra were scanned from 17155 eV to 17250 eV in 0.3 eV steps around white line. The emission spectrometer was performed for HERFD-XAS and resonant X-ray emission spectrum. The conventional XAS (total fluorescence yield XAS TFY-XAS) was acquired by a gas chamber at transition mode. The UO 2 powder, fabricated by China North Nuclear Fuel Company Limited, was annealed for 6 h under 5% H 2 and Ar atmosphere at 1273 K to ensure that the composition of UO 2 powder was stoichiometric. The UO 2 powder was oxidated to U 3 O 8 in air. Two standard samples (UO 2 and U 3 O 8 ) were used as the reference. The sample UO 2 was powdered in order to accelerate the oxidation process. Two asbestine cylinder was used to clamp the powder sample and reduce absorption of the incident X-ray. The in - situ cell then was placed at the intersection of X-ray line and Rowland circle. The heating appratus contains two probes inside the cell and a temperature controller that altered and maintained the temperature at the sample position. The cell has two more probes to provide 100% O 2 gas and pure He gas as protective gas. The entire cell was water cooled ( Fig 1b Fig 1b ). The sample UO 2 was heated to 300, 470, 520, 620, 770 and 970 K at O 2 atmosphere and kept at each temperature for 1 hour. Then, the HERFD-XAS was acquired at pure He atmosphere to ensure the oxide reaction no longer proceeded. 3 Results and Discussion 1 The spectra of HERFD-XAS and conventional XAS (TFY) of UO 2 at room temperature are shown in Fig 2(a) Fig 2(a) . The full width at half maximum (FWHM) of Peaks A and B for TFY XAS is 14 and 7 eV, respectively; while they are 9 and 6 eV for HERFD-XAS. Peak A is the white line. It is sensitive to the variation of valence state, and its shift provides information about valence state of oxidation products. Peak B originates from mutiple scatting, and the distance between A and B is inversely proportional to lattic spacing. So, the more narrow peaks, the more precisce lattic spacing will be obtained [ 17 17 ] . U 3 O 8 forms via mixed valence oxidation, and Peaks A and B of U 3 O 8 are wider than those of UO 2 . The HERFD-XAS of UO 2 and U 3 O 8 , as standard samples, are shown in Fig 2(b) Fig 2(b) . The peak intensities decreased gradually and the width increased. The intensity decrease of the main peaks could be due to the damaged symmetry of crystalline structure by the added O atoms [ 18 18 , 19 19 ] ., And the broadened main peaks could be originated from the combination of two valences of U 3 O 8 [ 20 20 ] . The spectrum of U 3 O 8 has a distinct shoulder peak at the higher energy side, due to mutiple scattering. Fig3 Fig3 shows the valence and structure changes of UO 2 powder samples heated in - situ in O 2 from 300 K to 970 K. The peak of HERFD-XAS at 300 K had the same shape as UO 2 . At 470 K the peak became broadened, with the disappearance of the sub-peak just after the main peak. The HERFD-XAS of UO 2 at 520 K was basically the same as that of 470 K, indicating that the oxidation process could not be maintained at lower temperatures, though some authors found that UO 2 powder above 470 K was transformed to U 3 O 7 /U 4 O 9 or similar structure. [ 21 21 ] At 620, 770 and 970 K, the HERFD-XAS spectra, without substantial changes, are similar to U 3 O 8 . Powder diffraction patterns of the sample before and after oxidation are shown in Fig 4 Fig 4 . In Fig 4(a) Fig 4(a) , at room temperature, the diffraction patterns are of characteristic diffraction peaks corresponding to the UO 2 structure (PDF-65-0285), while after oxidation ( Fig. 3b Fig. 3b ), the diffraction patterns show the same peak positions to U 3 O 8 structure (PDF-47-1493), indicating the transform from UO 2 to U 3 O 8 . 2 θ (°) × 4 Conclusion 1 The in- situ HERFD-XAS of UO 2 oxidation is helpful for analyzing complex products in oxidation process and providing precise XAS of U L 3 edge. The in - situ high energy-resolution X-ray absorption spectroscopy technology has been established successfully at SSRF. From the HERFD-XAS of UO 2 samples heated in - situ to 300–970 K and oxidized for one hour, the variation of valence states can be described and the changes of crystalline structure can be deduced. Temperature is basically the decisive factor in the oxidation process. The HERFD-XAS indicated structural changes agree with previous reports by other methods. References R. J. McEachern , P. Taylor ., A review of the oxidation of uranium dioxide at temperatures below 400 degrees . J.Nucl.Mater . 254 , 87 - 121 ( 1998 ). doi: 10.1016/S0022-3115(97)00343-7 http://doi.org/10.1016/S0022-3115(97)00343-7 . A review of the oxidation of uranium dioxide at temperatures below 400 degrees L. Desgranges , G. Baldinozzi , G. Rousseau et al ., Neutron diffraction study of the in situ oxidation of UO(2) . Inorganic chemistry . 48 , 7585 - 7592 ( 2009 ). doi: 10.1021/ic9000889 http://doi.org/10.1021/ic9000889 Neutron diffraction study of the in situ oxidation of UO(2) W. Q. Shi , L. Y. Yuan , C. Z. Wang et al ., Exploring Actinide Materials Through Synchrotron Radiation Techniques . Adv Mater . 26 , 7807 - 7848 ( 2014 ). doi: 10.1002/adma.201304323 http://doi.org/10.1002/adma.201304323 Exploring Actinide Materials Through Synchrotron Radiation Techniques T. Prüßmann , M. A. Denecke , A. Geist et al ., Comparative investigation of N donor ligand-lanthanide complexes from the metal and ligand point of view . Journal of Physics: Conference Series . 430 , 012115 ( 2013 ). doi: 10.1088/1742-6596/430/1/012115 http://doi.org/10.1088/1742-6596/430/1/012115 Comparative investigation of N donor ligand-lanthanide complexes from the metal and ligand point of view C. H. Booth , Y. Jiang , D. L. Wang et al ., Multiconfigurational nature of 5f orbitals in uranium and plutonium intermetallics . P Natl Acad Sci USA . 109 , 10205 - 10209 ( 2012 ). doi: 10.1073/pnas.1200725109 http://doi.org/10.1073/pnas.1200725109 Multiconfigurational nature of 5f orbitals in uranium and plutonium intermetallics T. Vitova , M. A. Denecke , J. Göttlicher et al ., Actinide and lanthanide speciation with high-energy resolution X-ray techniques . Journal of Physics: Conference Series . 430 , 012117 ( 2013 ). doi: 10.1088/1742-6596/430/1/012117 http://doi.org/10.1088/1742-6596/430/1/012117 Actinide and lanthanide speciation with high-energy resolution X-ray techniques K. O. Kvashnina , Y. O. Kvashnin S. M. Butorin . Role of resonant inelastic X-ray scattering in high-resolution core-level spectroscopy of actinide materials . Journal of Electron Spectroscopy and Related Phenomena . 194 , 27 - 36 ( 2014 ). doi: 10.1016/j.elspec.2014.01.016 http://doi.org/10.1016/j.elspec.2014.01.016 Role of resonant inelastic X-ray scattering in high-resolution core-level spectroscopy of actinide materials Connie J. Nelin , Paul S. Bagus Eugene S. Ilton . Theoretical analysis of the U L3-edge NEXAFS in U oxides . RSC Advances . 4 , 7148 ( 2014 ). doi: 10.1039/c3ra46738d http://doi.org/10.1039/c3ra46738d Theoretical analysis of the U L3-edge NEXAFS in U oxides K. Kvashnina , Y. Kvashnin , J. R. Vegelius et al ., Sensitivity to Actinide Doping of Uranium Compounds by Resonant Inelastic X-ray Scattering at Uranium L-3 Edge . Anal Chem . 87 , 8772 - 8780 ( 2015 ). doi: 10.1021/acs.analchem.5b01699 http://doi.org/10.1021/acs.analchem.5b01699 Sensitivity to Actinide Doping of Uranium Compounds by Resonant Inelastic X-ray Scattering at Uranium L-3 Edge J. G. Tobin , S. W. Yu , R. Qiao et al ., Covalency in oxidized uranium . Physical Review B . 92 ( 2015 ). doi: 10.1103/PhysRevB.92.045130 http://doi.org/10.1103/PhysRevB.92.045130 Covalency in oxidized uranium A. Walshe , T. Prussmann , T. Vitova et al ., An EXAFS and HR-XANES study of the uranyl peroxides [UO2(eta2-O2)(H2O)2].nH2O (n = 0, 2) and uranyl (oxy)hydroxide [(UO2)4O(OH)6].6H2O . Dalton transactions . 43 , 4400 - 4407 ( 2014 ). doi: 10.1039/c3dt52437j http://doi.org/10.1039/c3dt52437j An EXAFS and HR-XANES study of the uranyl peroxides [UO2(eta2-O2)(H2O)2].nH2O (n = 0, 2) and uranyl (oxy)hydroxide [(UO2)4O(OH)6].6H2O T. Vitova , K. O. Kvashnina , G. Nocton et al ., High energy resolution x-ray absorption spectroscopy study of uranium in varying valence states . Physical Review B . 82 ( 2010 ). doi: 10.1103/Physrevb.82.235118 http://doi.org/10.1103/Physrevb.82.235118 High energy resolution x-ray absorption spectroscopy study of uranium in varying valence states J. G. Tobin , S. W. Yu , C. H. Booth et al ., Oxidation and crystal field effects in uranium . Physical Review B . 92 ( 2015 ). doi: 10.1103/PhysRevB.92.035111 http://doi.org/10.1103/PhysRevB.92.035111 Oxidation and crystal field effects in uranium Xiao-Dong Wen , Matthias W. Löble , Enrique R. Batista et al ., Electronic structure and O K-edge XAS spectroscopy of U3O8 . Journal of Electron Spectroscopy and Related Phenomena . 194 , 81 - 87 ( 2014 ). doi: 10.1016/j.elspec.2014.03.005 http://doi.org/10.1016/j.elspec.2014.03.005 Electronic structure and O K-edge XAS spectroscopy of U3O8 Xing Gao , Songqi Gu , Qian Gao et al ., A high-resolution X-ray fluorescence spectrometer and its application at SSRF . X-Ray Spectrometry . 42 , 502 - 507 ( 2013 ). doi: 10.1002/xrs.2511 http://doi.org/10.1002/xrs.2511 A high-resolution X-ray fluorescence spectrometer and its application at SSRF H. S. Yu , X. J. Wei , J. Li et al ., The XAFS beamline of SSRF . Nucl Sci Tech . 26 ( 2015 ) The XAFS beamline of SSRF M. A. Denecke . Actinide speciation using X-ray absorption fine structure spectroscopy . Coordination Chemistry Reviews . 250 , 730 - 754 ( 2006 ). doi: 10.1016/j.ccr.2005.09.004 http://doi.org/10.1016/j.ccr.2005.09.004 Actinide speciation using X-ray absorption fine structure spectroscopy Laura Martel , Jean-Francois Vigier , Damien Prieur et al ., Structural Investigation of Uranium-Neptunium Mixed Oxides Using XRD, XANES, and17O MAS NMR . The Journal of Physical Chemistry C . 118 , 27640 - 27647 ( 2014 ). doi: 10.1021/jp507088t http://doi.org/10.1021/jp507088t Structural Investigation of Uranium-Neptunium Mixed Oxides Using XRD, XANES, and17O MAS NMR S. D. Conradson , D. Manara , F. Wastin et al ., Local structure and charge distribution in the UO2-U4O9 system . Inorganic chemistry . 43 , 6922 - 6935 ( 2004 ). doi: 10.1021/ic049748z http://doi.org/10.1021/ic049748z Local structure and charge distribution in the UO2-U4O9 system K. O. Kvashnina , S. M. Butorin , P. Martin et al ., Chemical state of complex uranium oxides . Physical review letters . 111 , 253002 ( 2013 ). doi: 10.1103/PhysRevLett.111.253002 http://doi.org/10.1103/PhysRevLett.111.253002 Chemical state of complex uranium oxides P.E. Blackburn , J. Weissbart , E.A. Gulbranson , Oxidation of uranium dioxide . J Phys Chem. 62 , 902 - 908 ( 1958 ). doi: 10.1021/j150566a002 http://doi.org/10.1021/j150566a002 Oxidation of uranium dioxide 10.1007/s41365-016-0155-x This work was supported by the National Nature Science Foundation of China (Nos. 11175244 and U1532259). 2016-03-08 2016-04-26 2016-05-12 2016-11-30 2017-01-01 2021-04-11 © China Science Publishing & Media Ltd. (Science Press), Shanghai Institute of Applied Physics, the Chinese Academy of Sciences, ChineseNuclear Society and Springer Nature Singapore Pte Ltd. 2017 This is a post-peer-review, pre-copyedit version of an article published in Nuclear Science and Techniques. The final authenticated version is available online at: http://dx.doi.org/10.1007/s41365-016-0155-x http://dx.doi.org/10.1007/s41365-016-0155-x . 2017 Nuclear Science and Techniques 01 28