Preparation and characterization of graphene nanoribbons

Huifang ZHANG; min LIU; Long YAN; Guojun YU; Xingtai ZHOU

doi:10.13538/j.1001-8042/nst.23.139-143

您当前的位置：

首页 >

文章列表页 >

Preparation and characterization of graphene nanoribbons

LOW ENERGY ACCELERATOR AND RADIATION APPLICATIONS | 更新时间：2021-01-29

- Preparation and characterization of graphene nanoribbons
- Preparation and characterization of graphene nanoribbons
- 核技术（英文版）
- 作者机构：
  
  1.Shanghai Institute of Applied Physics, Chinese Academy of Science, Shanghai 201800, China
  2.Graduate School of the Chinese Academy of Sciences, Beijing 100049, China
- 作者简介：
  
  Corresponding author. E-mail address: yanlong@sinap.ac.cn
  
  C
  o
  r
  r
  e
  s
  p
  o
  n
  d
  i
  n
  g
  
  a
  u
  t
  h
  o
  r
  .
  
  E
  -
  m
  a
  i
  l
  
  a
  d
  d
  r
  e
  s
  s
  :
  
  y
  a
  n
  l
  o
  n
  g
  @
  s
  i
  n
  a
  p
  .
  a
  c
  .
  c
  n
- 基金信息：
  
  National Basic Research Program of China;National Natural Science Foundation of China
- DOI：10.13538/j.1001-8042/nst.23.139-143 中图分类号：
- 纸质出版日期：2012-06-20，
  
  收稿日期：2011-03-14，
扫描看全文
引用本文
Huifang ZHANG, min LIU, Long YAN, 等. Preparation and characterization of graphene nanoribbons[J]. 核技术（英文版）, 2012, 23(3):139-143.

Huifang ZHANG, min LIU, Long YAN, et al. Preparation and characterization of graphene nanoribbons[J]. Nuclear Science and Techniques, 2012, 23(3):139-143.
Huifang ZHANG, min LIU, Long YAN, 等. Preparation and characterization of graphene nanoribbons[J]. 核技术（英文版）, 2012, 23(3):139-143. DOI： 10.13538/j.1001-8042/nst.23.139-143.

Huifang ZHANG, min LIU, Long YAN, et al. Preparation and characterization of graphene nanoribbons[J]. Nuclear Science and Techniques, 2012, 23(3):139-143. DOI： 10.13538/j.1001-8042/nst.23.139-143.

Preparation and characterization of graphene nanoribbons 1 2 first-author 1 2 1 corresp Corresponding author. E-mail address: yanlong@sinap.ac.cn Corresponding author. E-mail address: yanlong@sinap.ac.cn yanlong@sinap.ac.cn 1 1 Shanghai Institute of Applied Physics, Chinese Academy of Science, Shanghai 201800, China Shanghai Institute of Applied Physics, Chinese Academy of Science, Shanghai 201800, China Graduate School of the Chinese Academy of Sciences, Beijing 100049, China Graduate School of the Chinese Academy of Sciences, Beijing 100049, China Graphene nanoribbons (GNRs) have been synthesized by unzipping oxidized multiwalled carbon nanotubes. The thickness of the GNRs synthesized is ranged from mono-layer to four layers. The morphology of prepared GNRs is strongly dependent on structure and defects of the MWCNTs. The synchrotron radiation X-ray diffractions show the d (002 ) spacing of the GNRs decreases with the increase of the annealing temperature. This may be caused by the removing of water molecules and oxygen-containing functional groups in the GNRs. Graphene Nanoribbons Transmission electron microscope (TEM) Atomic force microscope (AFM) Raman spectrum Synchrotron radiation X-ray diffraction References Novoselov K S , Geim A K , Morozov S V , et al . Science , 2004 , 306 : 666 - 669 . Science Westervelt R M , Science , 2008 , 320 : 324 - 325 . Science Li X L , Wang X R , Zhang L , et al . Science , 2008 , 319 : 1229 - 1232 . Science Schedin F , Geim A K , Morozov S V , et al . Nat Mater , 2007 , 6 : 652 - 655 . Nat Mater Wang X , Zhi L J , Mullen K . Nano Lett , 2008 , 8 : 323 - 327 . Nano Lett Stankovich S , Dikin D A , Geoffrey H B D , et al . Nature , 2006 , 442 : 282 - 286 . Nature Chen Z H , Lin Y M , Michael J R , et al . Phys E , 2007 , 40 : 228 - 232 . Phys E Brey L , Fertig H A . Phys Rev B , 2006 , 73 : 235411 - 35415 . Phys Rev B Barone V , Hod O , Gustavo E S . Nano Lett , 2006 , 6 : 2748 - 2754 . Nano Lett Levente T , Gergely D , Philippe L , et al . 2008 , 3 : 397 - 401 . Melinda Y H , Barbaros O , Zhang Y B , et al . Rev Lett , 2007 , 98 : 206805 - 206808 . Rev Lett Sujit S D , Douglas R S , Samuel M K , et al . Nano Lett , 2008 , 8 : 1912 - 1915 . Nano Lett Ci L J , Xu Z P , Wang L L , et al . Nano Res , 2008 , 1 : 116 - 122 . Nano Res Campos L C , Manfrinato V R , Javier D S , et al . Nano Lett , 2009 , 9 : 2600 - 2604 . Nano Lett Dmitry V K , Amanda L H , Alexander S , et al . Nat Lett , 2009 , 458 : 872 - 876 . Nat Lett Jiao L Y , Zhang L , Wang X R , et al . Nat Lett , 2009 , 458 : 877 - 880 . Nat Lett Abraham G C , Fernando J R , Jessica C D , et al . Nano Lett , 2009 , 9 : 1527 - 1533 . Nano Lett Li J L , Konstantin N K , Michael J M , et al . Phys Rev Lett , 2006 , 96 : 176101 - 176104 . Phys Rev Lett Pulickel M A , Boris I Y , Nature , 2006 , 441 : 818 - 819 . Nature Goki EDA , Glovanni F , Manish C . Nat Nanotech , 2008 , 3 : 270 - 274 . Nat Nanotech Franco C , Giuseppe C , Giacomo P , et al . Carbon , 2010 , 48 : 2596 - 2602 . Carbon Ferrari A C , Robertson J . Phys Rev B , 2000 , 61 : 14095 - 14107 . Phys Rev B Becerril H A , Mao J , et al . ACS Nano , 2008 , 2 : 463 - 470 . ACS Nano 10.13538/j.1001-8042/nst.23.139-143 Supported by National Basic Research Program of China (Grant No. 2010CB832903) and National Natural Science Foundation of China (No.50902147) 2011-03-14 2012-06-20 2021-01-19 2012 Nuclear Science and Techniques 03 23

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Damage of DNA ends induced by mechanical force during AFM nano-manipulation