Mn DEPLETION IN THE SURFACE LAYER OF STAINLESS STEEL 304 LN AT THE TEMPERATURE 1200 K

Wang Wenmin，

Wang Qiuyu

pp.1-6

Published in print 01 Feb 1991

5100

The Mn component of stainless steel 304 LN has been found to be severely depleted in the surface layer during heating at the temperature 1200 K. The surface concentrations of Mn were reduced by about 2-3 orders of magnitude in comparison with the bulk value, as was revealed by a secondary ion mass spectroscopy (SIMS) system. And the Mn concentration gradient in the surface layer was examined, too, by SIMS. Massive preferential losses of Mn have been determined by using the catcher technique and proton induced X- ray emission (PIXE). A theoretical model has been proposed for calculating the surface concentration changes for a component in an alloy under heating. A comparison shows a good agreement between the calculation and experimental results from SIMS and catcher technique.

Preferential evaporationSurface depletionIon beam analysis

REFERENCES

[1]

R. Behrisch ed., Sputtering by particle bombardment II Springer, Berlin, Heidelberg, New York, Tokyo, 1983, P11.

[2]

R.E. Clausing et al., J. Nucl. Mater., 141- 143 (1986), 978.

[3]

B. Emmoth et al., J. Nucl. Mater., 162- 164 (1989), 941.

[4]

N. Yoshida et al., J. Nucl. Mater., 162- 164 (1989), 1082.

[5]

Wang Wenmin et al., J. Nucl. Mater., 162- 164 (1989), 422.

[6]

M. Fujitsuka et al., J. Nucl. Mater., 162- 164 (1989), 976.

[7]

Wang Wenmin et al., Nucl. Instr. Meth., B42 (1989), 29.

[8]

R. Hultgren et al., Selected values of thermodynamic properties of metals and alloys, Wiley, New York, 1963 and 1973.

[9]

A.S. Nowick, J. Appl. Phys., 22 (1951), 1182.

[10]

C.J. Smithells, Metals reference book, Interscience Publishers Inc., New York, 1949, p.390.